3D Multilayer Zirconia Blanks
Our zirconia blocks are compatible with different kinds of CAD/CAM system and manual system, such as Cercon system, Sirona Inlab system, KaVo system, Wieland system and Amann Girrbach AG system.
We choose the best zirconia powder and utilize a cold isostatic pressing system to form shapes,the main advantage of isostatic pressing is the uniform application of pressure, which lead to a very homogeneous density and shrinkage,yielding a very reproducible process.The production cost by using isostatic pressing is much higher than uniaxel dry pressing, but quality is also much higher.We try to provide high quality ,low cost zirconia blocks for all dental CAD/CAM milling system, support open architecture CAD/CAM milling system. We will sell lowest price on zirconia blocks and highest quality to all labs worldwide.
Simply to be Natural
| Layer | Proportion | Vickers Hardness(HV) | Strength(MPa) | Color | Translucency |
| Layer 1 | 30% | ≥1250 | ≥750 ,≤1250 | Shallow ↓ Deep | 43%—55% |
| Layer 2 | 15% |
| Layer 3 | 15% |
| Layer 4 | 20% |
| Layer 5 | 20% |
Characteristics:
Natural Color Transition, Pre-colored.
Top High Transmittance with Natural Gradient
Simple and Less Process of Production
Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA 3D multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three units, inlays, and onlays for anterior and posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.
Chemical Composition
| ZrO2+HfO2 | ＞94wt% |
| Y2O3 | 5.3wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.5wt% |
Properties
Sintering Density :6.0g/cm³
Bending Strength:≥750MPa
Vickers Hardness:1250HV
Chemical Solubility:＜100μg/m²
| Sintering step | Temperature range(℃) | Time(h) |
| paragraph 1 | 20-900 | 1.5 |
| paragraph 2 | 900-900 | 0.5 |
| paragraph 3 | 900-1530 | 4.0 |
| paragraph 4 | 1530-1530 | 2.0 |
| paragraph 5 | 1530-800 | 2.0 |
| paragraph 6 | 800-Natural cooling 100 | Draw a charge |
XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide
Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over
30,000 square meters R&D and production base.
In the past 10 years, XTCERA has sold out about 4000 units dental milling machines and
supplied over 1,000,000 pieces of dental Zirconia blanks per year in the global dental market.