Feature :
high flexural strength, fracture resistance, exceptional durability, and easy milling properties with precision. Pre-shaded zirconia disc consisting of three pre-colored layers Easy Handling: Polish or Glaze after Sintering Ideal for full contour crowns and bridges
Benefits:
Reduce preparation dramatically No need for porcelain Restoration seated firmly Eliminates the possibility of porcelain chipping No need to take out restoration under imaging medical examinations fast and efficient sintering technology Unique coloring changing effect No need for coloring liquids For open systems with different sizes such as Wieland, Sirona, Zirconzahn, Kavo, Lava, Amann Girrbach, Cercon, Dentmill etc.
Pre-shaded zirconia blanks
Preshade zirconia blanks are researched and manufactured by XTCERA . We select high quality exported zirconium powder, mixing with different colored powder, pressing ,shaping ,pre-sintering to make the zirconia blanks , helps solve the problems like uneven colors , spot, over obvious and negative color difference between the front and the back.
The zirconia blank is non-toxic and non-radioactive with excellent biological properties, teeth color is like the real teeth with good permeability and aesthetics. It is with high strength, good toughness and excellent wear resistance, X-cera pre-shaded zirconia blank is the raw material with excellent property for making crowns.
Applicable system: wieland,sirona,kavo,lava,amann girrbach and cercon,etc.
Indications:Veneers, anterior crown/coping
Sintering temperature:1530℃
Shades:A1,A2,A3,A3.5,A4,B1,B2,B3,B4,C1,C2,C3,C4,D2,D3,D4
Density(after sintering):6.05±0.05g/cm3
Bending strength(after sintering):＞900MPa
Sintering curve: Room temprature→10℃/min to 900℃(preserve for 30min) →3.5 ℃/min to 1530℃(preserve for 2h) →12 ℃/min to 800℃ →follow the furnace cooling to room temperature