TT Multilayer Zirconia Block Wear Resistant For Open Cad Milling System

Product Categories

Dental Zirconia Block [19]
Multilayer Zirconia Block [11]
High Translucency Zirconia [12]
Dental Zirconia Blank [41]
Zirconium Oxide Ceramic [9]
Dental Base Metal Alloys [8]
Dental Zirconia Milling Machine [27]
5 Axis Dental Milling Machine [22]
Dental Milling Burs [6]
3D Printing Metal Powder [4]
Dental Wax Block [2]
Zirconia Coloring Liquid [6]

Shenzhen Xiangtong Co.,Ltd.

Contact Now

TT Multilayer Zirconia Block Wear Resistant For Open Cad Milling System

Name: TT Multilayer Zirconia Block Wear Resistant For Open Cad Milling System
Brand: XTCERA
Price: 1 USD

China TT Multilayer Zirconia Block Wear Resistant For Open Cad Milling System wholesale

Brand Name : XTCERA

Model Number : 98*14

Certification : FDA,CE,SFDA,ISO 19485

Place of Origin : CHINA

MOQ : 50

Price : Negotiable

Payment Terms : T/T, Western Union

Delivery Time : 5-8 working days

Packaging Details : box

Feature : good translucent,comfortable

Translucency : 55%

Size : 98*14

Vickers Hardness : 1250HV

Sintering Density : ≥6.0g/cm³

Usage : Denture Teeth

Contact Now

Multilayer TT Zirconia Blanks

Characteristics:

Top High Transmittance

Natural Color Transition, Pre-colored.

Simple and Less Process of Production

Available in all classic VITA 16 shades (A1 to D4)
Indications
XTCERA TT Multilayer is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, inlays and onlays restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.

Perfect Your Smile!

Layer	Proportion	Vickers Hardness(HV)	Strength(MPa)	Color	Translucency
Layer 1	30%	≥1250	≥750	Shallow ↓ Deep	55%
Layer 2	15%
Layer 3	15%
Layer 4	20%
Layer 5	20%

Sintering:
► Max Heating rate:10℃ per minute;
► Final temperature:1450℃;
► Holding time at final temperature:2 hours;
► Cooling should be done without temperature control in closed furnace;
► Never open the furnace before it has reached a temperature of less than 80℃ to avoid thermal shocks.

Chemical Composition

Component	Content
ZrO2+HfO2	＞90.5wt%
Y2O3	9.28wt%
AL2O3	＜0.5wt%
Other Oxides	＜0.5wt%

Properties

Projects	Detection result
Sintering Density	≥6.0g/cm³
Bending Strength	≥750MPa
Transmittance	55%
Vickers Hardness	1250HV

Sintering step	Temperature range (℃)	Time(h)
paragraph 1	20-900	1.5
paragraph 2	900-900	0.5
paragraph 3	900-1450	3.0
paragraph 4	1450-1450	2.0
paragraph 5	1450-800	1.0
paragraph 6	800-Natural cooling 100	Finished

Product Tags:

ultra translucent zirconia

cerec zirconia blocks

TT Multilayer Zirconia Block Wear Resistant For Open Cad Milling System Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Shenzhen Xiangtong Co.,Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!