Multilayer SHT Zirconia Blanks
Feature :
high flexural strength, fracture resistance, exceptional durability, and easy milling properties with precision. Pre-shaded zirconia disc consisting of three pre-colored layers Easy Handling: Polish or Glaze after Sintering Ideal for full contour crowns and bridges
Benefits:
Reduce preparation dramatically No need for porcelain Restoration seated firmly Eliminates the possibility of porcelain chipping No need to take out restoration under imaging medical examinations fast and efficient sintering technology Unique coloring changing effect No need for coloring liquids For open systems with different sizes such as Wieland, Sirona, Zirconzahn, Kavo, Lava, Amann Girrbach, Cercon, Dentmill etc.
Natural Color Transition,No Need Dyeing
| Layer | Proportion | Vickers
Hardness(HV) | Strength(MPa) | Color | Translucency |
| Layer 1 | 30% | ≥1250 | ≥1050 | Shallow
↓
Deep | 47% |
| Layer 2 | 15% |
| Layer 3 | 15% |
| Layer 4 | 20% |
| Layer 5 | 20% |
Available in all classic VITA 16 shades (A1 to D4)
Indications For Use
XTCERA SHT Multilayer is intended for the fabrication and preparation of copings, full
anatomical/ full contour crowns, bridges up to three uints, inlays, and onlays for anterior and
posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.
Chemical Composition
| Component | Content |
| ZrO2+HfO2 | ＞90wt% |
| Y2O3 | 4.5-9.5wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.2wt% |
Properties
| Projects | Detection result |
| Sintering Density | ≥6.0g/cm³ |
| Bending Strength | ≥1050MPa |
| Vickers Hardness | 1293HV |
| Chemical Solubility | ＜100μg/m² |
Multilayer Preshaded 4D Translucent Zirconia, a revolution in Dental Zirconia. 4D Multilayer has 5 layers of Chroma transitioning from gingiva to incisal.
1. Gradient 43-49% Translucency.
2. Gradient 650-1100 Mpa Bending Strength
3. Suitable for full contour crown and bridge.
Indications
Monolithic – Anterior, Posterior
Monolithic – Bridge
Coping – Crown, Bridge
Implant Structure
Veneer
Product Tags:
|
|
High Translucency 47% Dental Zirconia Discs 1050 Mpa High Bending Strength Images
|