Unique 3D White, which leaves you more space of dyeing and imagination!
| layer |
Proportion |
Vickers
Hardness(HV)
|
Strength(MPa) |
Translucency |
| layer 1 |
20% |
≥1250 |
≥750 |
55%
↑
43%
|
| layer 2 |
20% |
≥1270 |
≥920 |
| layer 3 |
20% |
≥1290 |
≥950 |
| layer 4 |
20% |
≥1310 |
≥1000 |
| layer 5 |
20% |
≥1350 |
≥1100 |
Features:
Unique Dyeing System
White but Translucent with Natural Gradient
Flexible Coloring to Make Teeth More Natural
Indications
XTCERA 3D White is intended for the fabrication and preparation of copings, full anatomical/ full
contour crowns, bridges up to three uints, inlays, and onlays for anterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.
Chemical Composition
| Component |
Content |
| ZrO2+HfO2 |
＞90.5wt% |
| Y2O3 |
9.28wt% |
| AL2O3 |
＜0.5wt% |
| Other Oxides |
＜0.5wt% |
Properties
| Projects |
Detection result |
| Sintering Density |
≥6.0g/cm³ |
| Bending Strength |
≥750MPa |
| Vickers Hardness |
1250HV |
| Chemical Solubility |
＜100μg/m² |
XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide
Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over
30,000 square meters R&D and production base.
In the past 10 years, XTCERA has sold out about 4000 units dental milling machines and
supplied over 1,000,000 pieces of dental Zirconia blanks per year in the global dental market.
We believe quality is the life of product and trust is the foundation of business relation